Ferrosilikon temir va kremniydan tashkil topgan temir qotishmasi.
Ferrosilikon ferrosilikon deb ham ataladi. Bu xom ashyo sifatida koks, po'lat qoldiqlari, kvarts (yoki kremniy) dan tayyorlangan va elektr pechda eritilgan temir-kremniy qotishmasi. U po'lat sanoati, quyish sanoati va boshqa sanoat ishlab chiqarishida keng qo'llaniladi.
ferrosilikon 75
Odatda ishlatiladigan navlar: 65#, 75A#, 75B#, qattiq 75# (kremniy 75% dan katta yoki unga teng)
|
Turi |
Elementlar tarkibi |
|||||||
|
% Si |
% Al |
% Ca |
% Mn |
% Cr |
% P |
% S |
% C |
|
|
FeSi75Al0.5-A |
74.0-80.0 |
0.5 |
1.0 |
0.4 |
0.3 |
0.035 |
0.02 |
0.1 |
|
FeSi75Al0.5-B |
72.0-80.0 |
0.5 |
1.0 |
0.5 |
0.5 |
0.04 |
0.02 |
0.2 |
|
FeSi75Al1.0-A |
74.0-80.0 |
1.0 |
1.0 |
0.4 |
0.3 |
0.035 |
0.02 |
0.1 |
|
FeSi75Al1.0-B |
72.0-80.0 |
1.0 |
1.0 |
0.5 |
0.5 |
0.04 |
0.02 |
0.2 |
|
FeSi75Al1.5-A |
74.0-80.0 |
1.5 |
1.0 |
0.4 |
0.3 |
0.035 |
0.02 |
0.1 |
|
FeSi75Al1.5-B |
72.0-80.0 |
1.5 |
1.0 |
0.5 |
0.5 |
0.04 |
0.02 |
0.2 |
|
FeSi75Al2.0-A |
74.0-80.0 |
2.0 |
1.0 |
0.4 |
0.3 |
0.035 |
0.02 |
0.1 |
|
FeSi75Al2.0-B |
74.0-80.0 |
2.0 |
1.0 |
0.4 |
0.3 |
0.04 |
0.02 |
0.1 |
|
FeSi75Al2.0-C |
72.0-80.0 |
2.0 |
0.5 |
0.5 |
0.04 |
0.02 |
0.2 |
|
|
FeSi75-A |
74.0-80.0 |
0.4 |
0.3 |
0.035 |
0.02 |
0.1 |
||
|
FeSi75-B |
74.0-80.0 |
0.4 |
0.3 |
0.04 |
0.02 |
0.1 |
||
|
FeSi75-C |
72.0-80.0 |
0.5 |
0.5 |
0.04 |
0.02 |
0.2 |
||
|
FeSi65 |
65.0-72.0 |
0.6 |
0.5 |
0.04 |
0.02 |
|||
|
FeSi45 |
40.0-47.0 |
0.7 |
0.5 |
0.04 |
0.02 |
|||
Odatda ishlatiladigan holat: tabiiy blok, qalinligi taxminan 100 mm. (Tashqi ko'rinishida yoriqlar bormi, qo'l bilan tegizilganda rangi o'chib ketadimi, urilganda tiniq bo'ladimi, qalinligi va ko'ndalang kesmasi kulrang oq rangda bo'ladimi)
Tez-tez ishlatiladigan qadoqlash: quyma yoki tonna sumkali qadoqlash.
temir kremniy 72
Eslatma: Ferrosilikon namlikdan qo'rqadi. Tabiiy bloklar suv ta'sirida osonlikcha maydalanadi va keyinchalik kremniy miqdori kamayadi.